不銹鋼埋弧焊絲及焊劑 |
|||||||||||||||||||
品名 | 規(guī)格(mm) | 符合標準 | 焊接位置 | 電流類型 | 典型的熔敷金屬化學成分例值(wt%) | 典型的熔敷金屬機械性能例值 | 應用 | ||||||||||||
C | Mn | Si | P | S | Cr | Ni | Others | 屈服強度(Mpa) | 抗拉強度(Mpa) | 延伸率(%) | 沖擊(J) | ||||||||
WWS-308??????????? WXS-601 | 2.5/3.2/4.0 | NB/T F308-H0Cr21Ni10 GB/T S F308L FB-S308L |
PA,PB,PC | DC+ | 0.040 | 1.77 | 0.37 | 0.021 | 0.008 | 20.28 | 9.28 | - | - | - | - | 585 | 41 | - | 18%Cr-8%Ni化學成分,焊接性優(yōu)良。? |
WWS-308L??WXS-601 | 2.5/3.2/4.0 | NB/T F308L-H00Cr21Ni10 GB/T S F308 FB-S308 |
PA,PB,PC | DC+ | 0.039 | 1.77 | 0.45 | 0.022 | 0.010 | 19.55 | 9.35 | - | - | - | - | 590 | 39 | - | 低C-18%Cr-8%Ni化學成分,焊接性優(yōu)良。? |
WWS-309L??WXS-601 | 2.5/3.2/4.0 | NB/T F309L-H022Cr24Ni13 GB/T S F309L FB-S309L |
PA,PB,PC | DC+ | 0.026 | 1.55 | 0.36 | 0.025 | 0.011 | 22.95 | 12.51 | - | - | - | - | 570 | 36 | - | 低C-22%Cr-12%Ni化學成分,焊接性優(yōu)良,適用于不銹鋼與碳鋼或低合金鋼的異材焊接。 |
WWS-316L??WXS-601 | 2.5/3.2/4.0 | NB/T F316L-H00Cr19Ni12Mo2 GB/T S F316L FB-S316L |
PA,PB,PC | DC+ | 0.025 | 1.31 | 0.55 | 0.026 | 0.012 | 18.81 | 11.50 | Mo:2.03 | - | - | - | 555 | 40 | - | 低C-18%Cr-12%Ni-2%Mo化學成分,焊接性優(yōu)良。? |
WWS-347?WXS-667 | 2.5/3.2/4.0 | NB/T F347-H06Cr21Ni10Nb GB/T S F347 FB-S347 |
PA,PB,PC | DC+ | 0.044 | 1.87 | 0.81 | 0.018 | 0.012 | 20.03 | 9.83 | Nb:0.42 | - | - | - | 555 | 36 | - | 18%Cr-11%Ni-Nb化學成分,焊接性優(yōu)良,抗晶間腐蝕性能優(yōu)異。 |
不銹鋼埋弧焊絲及焊劑 |
|||||||||||||||||||
品名 | 規(guī)格(mm) | 符合標準 | 焊接位置 | 電流類型 | 典型的熔敷金屬化學成分例值(wt%) | 典型的熔敷金屬機械性能例值 | 應用 | ||||||||||||
C | Mn | Si | P | S | Cr | Ni | Others | 屈服強度(Mpa) | 抗拉強度(Mpa) | 延伸率(%) | 沖擊(J) | ||||||||
WWS-308??????????? WXS-601 | 2.5/3.2/4.0 | NB/T F308-H0Cr21Ni10 GB/T S F308L FB-S308L |
PA,PB,PC | DC+ | 0.040 | 1.77 | 0.37 | 0.021 | 0.008 | 20.28 | 9.28 | - | - | - | - | 585 | 41 | - | 18%Cr-8%Ni化學成分,焊接性優(yōu)良。? |
WWS-308L??WXS-601 | 2.5/3.2/4.0 | NB/T F308L-H00Cr21Ni10 GB/T S F308 FB-S308 |
PA,PB,PC | DC+ | 0.039 | 1.77 | 0.45 | 0.022 | 0.010 | 19.55 | 9.35 | - | - | - | - | 590 | 39 | - | 低C-18%Cr-8%Ni化學成分,焊接性優(yōu)良。? |
WWS-309L??WXS-601 | 2.5/3.2/4.0 | NB/T F309L-H022Cr24Ni13 GB/T S F309L FB-S309L |
PA,PB,PC | DC+ | 0.026 | 1.55 | 0.36 | 0.025 | 0.011 | 22.95 | 12.51 | - | - | - | - | 570 | 36 | - | 低C-22%Cr-12%Ni化學成分,焊接性優(yōu)良,適用于不銹鋼與碳鋼或低合金鋼的異材焊接。 |
WWS-316L??WXS-601 | 2.5/3.2/4.0 | NB/T F316L-H00Cr19Ni12Mo2 GB/T S F316L FB-S316L |
PA,PB,PC | DC+ | 0.025 | 1.31 | 0.55 | 0.026 | 0.012 | 18.81 | 11.50 | Mo:2.03 | - | - | - | 555 | 40 | - | 低C-18%Cr-12%Ni-2%Mo化學成分,焊接性優(yōu)良。? |
WWS-347?WXS-667 | 2.5/3.2/4.0 | NB/T F347-H06Cr21Ni10Nb GB/T S F347 FB-S347 |
PA,PB,PC | DC+ | 0.044 | 1.87 | 0.81 | 0.018 | 0.012 | 20.03 | 9.83 | Nb:0.42 | - | - | - | 555 | 36 | - | 18%Cr-11%Ni-Nb化學成分,焊接性優(yōu)良,抗晶間腐蝕性能優(yōu)異。 |